Electrical and mechanical properties enhancing of PMMA and PA6 by functionalized MWCNTs addition
PA6 and PMMA polymers with different MWCNTs addition (5, 7 and 9 wt %) were synthetized through casting solution, resulting in improvement properties in contrast to pristine polymers. SEM images showed the MWCNTs embedded into polymeric matrices. D, G and G´ bands of MWCNTs were confirmed by Raman spectroscopy and functional groups observed in both nanocomposites by FTIR demonstrated a strong interaction. A significant increasing in electrical conductivity and microhardness was observed in all the nanocomposites. Major microhardness values were obtained in MWCNTs/PA6 (50 HV) however the MWCNTs/PMMA nanocomposites showed the highest electrical conductivity value (6.4×10−4 S/cm).